Product Details
Grade 304 Chequered is the standard "18/8" stainless; it is the most versatile and most widely used Chequered, available in a wider range of products, forms and finishes than any other. Stainless Steel 304 Chequered Plates has excellent forming and welding characteristics. The balanced austenitic structure of Grade 304 enables it to be severely deep drawn without intermediate annealing, which has made this grade dominant in the manufacture of drawn stainless parts such as sinks, hollow-ware and saucepans. For these applications it is common to use special "304DDQ" (Deep Drawing Quality) variants. Grade 304 Chequered Plate is readily brake or roll formed into a variety of components for applications in the industrial, architectural, and transportation fields. Grade 304 also has outstanding welding characteristics. Post-weld annealing is not required when welding thin sections.
Standard : ASTM / ASME A240 / SA240
Size : 1000 mm x 2000 mm, 1220 mm x 2440 mm, 1500 mm x 3000 mm, 2000 mm x 2000 mm, 2000 mm x 4000 mm
Thickness : 0.1mm to 12 mm Thk
Form : Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Strip, Flats, Blank (Circle), Ring (Flange)
Finish : Hot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated)
Hardness : Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc.
| STANDARD | WERKSTOFF NR. | UNS | JIS | BS | GOST | AFNOR | EN |
| SS 304 | 1.4301 | S30400 | SUS 304 | 304S31 | 08Х18Н10 | Z7CN18-09 | X5CrNi18-10 |
| Element | SS 304 |
| C | 0.08 max |
| Mn | 2 max |
| Si | 0.75 max |
| P | 0.045 max |
| S | 0.030 max |
| Cr | 18 – 20 |
| Ni | 8 – 11 |
| Element | SS 304 |
| Density | 8.0 g/cm3 |
| Melting Point | 1400 °C (2550 °F) |
| Tensile Strength | Psi – 75000 , MPa – 515 |
| Yield Strength (0.2%Offset) | Psi – 30000 , MPa – 205 |
| Elongation | 35 % |
Automotive
Railway & Transport
Architecture, Building & Construction
Chemical & Petrochemical Industries
Pharmaceutical
Energy and Power
Oil and Gas Industries
Kitchenware and Food Processing Industries
Plumbing And Overhead Water Tanks
Người liên hệ: Mr. Gao Ben
Tel: +86-18068357371
Fax: 86-0510-88680060